BEBERAPA LANGKAH UNTUK MEMPANJANGKAN HAYAT PERKHIDMATAN CASTABLES PELAPIS DANDANG

Pencurian refraktori dandang katil terbendalir yang beredar adalah bahagian penting yang mempengaruhi kitaran operasi dandang. Tahap refraktori, kekuatan terma, kadar pengecutan, kualiti tuang, penyelenggaraan dan ketuhar castable secara langsung mempengaruhi kekuatan dan hayat dinding dandang. Mempengaruhi kitaran operasi dandang, dan pada masa yang sama, kualiti pemeliharaan dan perlindungan haba di luar badan relau menyekat pengembangan dandang, terutamanya pada musim sejuk apabila suhu lebih rendah daripada tolak 5 darjah, disebabkan oleh pengembangan tak segerak keseragaman, ia adalah mudah untuk menyebabkan tekanan dalam sambungan kimpalan bahagian yang berkaitan saluran paip. Penutupan relau berpusat dan bocor mengurangkan kitaran operasi, meningkatkan bilangan relau dan input relau, menjejaskan operasi lancar unit sistem, dan meningkatkan risiko operasi. Melalui masalah yang ditemui semasa operasi sebenar dandang dan semasa penutupan dan penyelenggaraan, castable telah rosak sebahagiannya semasa pembinaan, dan tiada jurang pengembangan terpelihara semasa pembinaan dan penebat luaran yang tidak betul menyebabkan perbezaan suhu yang besar antara bahagian dalam dan luar. Sebab utama kerosakan adalah keretakan. Dengan membincangkan mekanisme bahan, menggunakan bahagian, dan mengukuhkan kawalan pautan, diharapkan dapat mencapai tujuan untuk meningkatkan hayat perkhidmatan.
Analisis Situasi Semasa Katil Terbendalir Beredar
Kapasiti beban dandang loji janakuasa lombong arang batu sendiri adalah agak rendah, kebanyakannya adalah dandang katil terbendalir yang beredar dengan sifat penggunaan menyeluruh yang menggunakan bahan api yang lebih rendah, dan kapasiti penyejatan kebanyakannya 75t/j dan 130t/ h. Disebabkan penggunaan bahan api yang lebih rendah, nilai kalori adalah rendah, kandungan abu adalah tinggi, muncung sanga dandang, sudut nyalaan terlipat relau, castable tahan haus pada kaki lajur penyuap arang batu dan pemisah siklon terdedah kepada retak, haus dan lusuh, tahan haus Castable adalah faktor utama yang menyekat operasi jangka panjang dandang; pemilihan bahan perlindungan dan penebat luaran dan kualiti pembinaan dandang adalah kehilangan haba, dan sambungan kimpalan di mana kepekatan tegasan mudah disebabkan oleh pemanasan relau tempat dan penurunan mendadak dalam suhu ambien luaran. Pada masa yang sama, dengan keperluan perlindungan alam sekitar yang semakin ketat, apabila Ca/S=1.5-2.0 daripada dandang dengan penyahsulfuran suntikan kalsium dalam relau, kecekapan penyahsulfuran boleh mencapai {{8 }} peratus, kadar penggunaan serbuk batu kapur adalah hampir dua kali ganda berbanding dandang katil terbendalir konvensional, tetapi input desulfurizer meningkatkan jumlah bahan katil dan bahan beredar, dan meningkatkan haus castable dinding relau. Kehausan castable tahan haus mendedahkan dinding filem yang disejukkan air dan plat pelindung luar. Dalam kes yang teruk, plat pengawal terbakar, cacat, retak, dan kelengkapan paip galas tekanan bocor disebabkan kekuatan haus yang berkurangan, yang sangat memendekkan tempoh operasi, meningkatkan kadar kemalangan, dan menjejaskan pengeluaran Selamat dan bahan meningkat dan input buruh.
Analisis prestasi castable tahan haus dalam bahagian penting dandang
The furnace wall of the low magnification circulating fluidized bed boiler adopts the tube-laying light furnace wall, the cyclone separator, the inclined flue, the furnace top and the tail flue are built with refractory castables, phosphate bricks and aluminum silicate insulation materials. High-strength composite refractory castables are poured into the lower part of the membrane-type water-cooled wall of the furnace. Different forms of refractory materials are selected and used according to the fluidization rate, flue gas flow rate, and refractory degree, so as to reduce construction and maintenance costs while ensuring service life and wear resistance. . The wear-resistant castable is made by mixing oxides and binders. The fluidized bed boiler furnace uses high-strength refractory castables with good fluidity. There are great differences in wear resistance, etc., which affect the boiler operation cycle. The refractory materials in the high temperature zone of the circulating fluidized bed boiler are mainly high-strength refractory castables. The main components are Al2O3+TiO2, and Portland cement is blended in a certain proportion. Due to different processes, the refractoriness, linear expansion rate, wear resistance There is a big difference in strength, which affects the service life of the boiler. The composition (quality parameter) of the alum clinker should be Al2O3>60 peratus, SiO2<20%, Fe2O3<3%; the concrete should be dried to remove moisture, and the basic refractory Do not dry when cemented with phosphoric acid. When acid and neutral refractories are cemented with phosphoric acid, immediately dry at 350℃<450℃<. (The phosphate solution is adjusted with 50% phosphoric acid and industrial aluminum hydroxide in a mass ratio of 7:1) According to the comparison of the physical properties of the castable, the phosphate refractory castable has high strength and hardness, and has a good linear expansion coefficient. To meet the requirements of use, it is fixed on the pressure furnace wall by 1Cr18Ni9Ti stainless steel nails, and has good adhesion with the furnace wall 20G membrane water cooling wall.
Faktor utama yang mempengaruhi hayat castable tahan haus
1. Pengaruh struktur dandang
Mengikut ciri-ciri struktur dandang, dandang katil terbendalir yang beredar terutamanya menggunakan abu yang dibakar di dalam relau untuk naik bersama udara panas, dan siklon di pintu keluar relau menghasilkan pemotongan berputar dan tenggelam, dan bahan kembali mengalir. ke dalam relau melalui udara kembali, suhu tiga bahagian dengan suhu dandang yang lebih tinggi semasa operasi biasa ialah: (1), larian relau: 900 darjah (2), alur keluar relau: 892 darjah ⑶, pemisah siklon: 852 darjah . Halaju asap ialah: relau 5m/s, keluar relau 5m/s, dan pemisah siklon 9.5m/s. Suhu yang lebih tinggi dan halaju asap akan meningkatkan haus castable tahan haus, dan rawatan tahan haus mesti diperkukuh.
2. Kesan bahan api
Bahan api dandang ialah hasil sampingan daripada gangue pembasuh loji penyediaan arang batu, lendir arang batu dan pembasuhan arang batu campuran, dengan nilai kalori yang rendah dan kandungan abu yang tinggi, yang akan menyebabkan haus pada castable tahan haus dan paip dinding yang disejukkan air pada relau. semasa pembakaran mendidih. Kehausan castable tahan haus pemisah siklon dan bahan kembali adalah amat serius. Kerosakan pada castable dengan mudah boleh menyebabkan plat pengawal luar dipanaskan secara langsung, cacat dan retak, dan fenomena kebocoran asap dan kebocoran abu berlaku. Menjejaskan operasi biasa dandang, dan persekitaran tapak menjadi lebih teruk.
3. Kesan kualiti pembinaan
Kualiti pembinaan adalah faktor utama yang mempengaruhi hayat perkhidmatan castable tahan haus dandang. Langkah-langkah pembinaan yang diperlukan tidak diambil untuk pembinaan bermusim, proses pembinaan tidak memenuhi keperluan standard, tempoh penyelenggaraan adalah pendek, dan ketuhar tidak boleh dibakar mengikut ketat dengan lengkung ketuhar yang diberikan, mengakibatkan daya ikatan dan rintangan haus. castable tahan haus tidak dapat memenuhi keperluan reka bentuk.
4. Pengaruh turun naik beban pada castable semasa peringkat permulaan, penutupan dan operasi dandang
Kawalan yang lemah terhadap kadar pemanasan dan penyejukan apabila dandang dipanaskan dan ditutup untuk menyejukkan akan menyebabkan perbezaan suhu yang besar antara bahagian dalam dan luar membentuk tegasan haba yang besar. Kegagalan peralatan penyusuan arang batu dan perubahan besar dalam kualiti arang batu semasa operasi akan menyebabkan suhu relau berubah-ubah. Terdapat turun naik suhu katil sebanyak 150 darjah . Pertama, ia menjejaskan parameter stim. Kedua, isipadu udara perlu diselaraskan dalam masa. Turun naik nisbah udara kepada arang batu menyebabkan gangguan keadaan pembakaran, yang menyebabkan castable terhakis kepada api dan menjejaskan penggunaan castable tahan haus. kehidupan.